Mn1-xCuxO2/ reduced graphene oxide nanocomposites: Synthesis,characterization, and evaluation of visible light mediated catalytic studies

The narrow optical band gap, higher electrical conductivity, and wider-absorption range are three key features that a good photocatalyst must possess. Herein, we have fabricated Cu-doped MnO₂ (Mn_1-xCu_xO₂) nanostructure by facile wet chemical approach and formed its nanocomposite with r-GO (Mn_1-xCu_xO₂/r-GO) via ultra-sonication approach. The successful replacement of host metal ions (Mn⁴⁺) with the dopant metal ions (Cu²⁺) was supported with the PXRD, FT-IR, and EDX characterizations. The effect of Cu-doping on the band gap and r-GO matrix on the conductivity of the fabricated nanocomposite was also evaluated via Tauc plots and I–V tests, respectively. The photocatalytic efficiency of the fabricated photocatalysts was tested and compared against the methylene blue (MB) under visible light irradiation. The photocatalytic experiments revealed that Mn_1-xCu_xO₂/r-GO photocatalyst exhibited superior photocatalytic aptitude than that of pristine MnO₂ and Mn_1-xCu_xO₂ photocatalysts. More precisely, the Mn_1-xCu_xO₂ photocatalysts degraded 86.89% MB dye at the rate of 0.021 min^?1 after a 90-min exposure to the visible light. Observed superior catalytic activity of the nanocomposite can be attributed to the synergistic effects between the Cu doped MnO₂ and r-GO nanosheets that resulted in its narrow band-gap (2.19 eV) and excellent conductivity (2.217 × 10^?2 Scm^?1).