利用FePt/Au多层膜结构制备垂直磁记录L10-FePt薄膜

利用磁控溅射方法在100℃的MgO单晶基片上制备了［FePt/Au］₁₀多层膜，并研究了采用FePt/Au多层膜结构对FePt薄膜的有序化温度、矫顽力（H_C）、垂直磁各向异性、晶粒尺寸以及颗粒间磁交换耦合作用的影响.磁性测试结果表明：FePt/Au多层膜在退火后具有较高的H_C、良好的垂直磁各向异性、较小的晶粒尺寸且无磁交换耦合作用.截面高分辨电镜分析表明：Au可以缓解MgO和FePt之间较大的晶格错配，从而促进薄 关键词： 0-FePt薄膜')" href="#">L1₀-FePt薄膜 有序化温度 垂直磁各向异性 磁交换耦合作用

Preparation of L10-FePt film for perpendicular magnetic recording media by using FePt/Au mutilayers

FePt/Au mutilayers were deposited on 100℃ MgO（001） single crystal substrate by magnetron sputtering. The influence of the FePt/Au multilayer structure on the ordering temperature, coercivity （Ｈ_C）, perpendicular magnetic anisotropy （PMA）, FePt grain size and interparticle exchange coupling （IEC） of films were studied. Results show that the film possesses high Ｈ_C, excellent PMA, small grain size and weak interparticle exchange coupling after annealing. The results of HRTEM reveal that Au can relieve mismatch between MgO and FePt lattices, leading to excellent PMA. Moreover, the FePt/Au interface energy, the stress energy due to the mismatch between FePt and Au lattices and the diffusion of Au atoms promote the ordering of FePt film. This leads to the decrease of ordering temperature and considerable increase of Ｈ_C. Au atoms partly diffuse to the boundaries of FePt phase and function as grain finer and particle isolator, which decrease the FePt grain size and IEC.