A calorimetric study of precipitation in aluminum alloy 2219

Precipitate microstructures in aluminum alloy 2219 were characterized using transmission electron microscopy (TEM) and differential scanning calorimetry (DSC). The DSC signatures of individual precipitate phases were established by comparing the DSC and TEM results from samples that had been aged such that only one precipitate phase was present. These signatures were then used to analyze the commercial tempers. It was found that DSC could readily distinguish between the T3, T4, T6, T8 and O tempers but could not distinguish amongst T81, T851 and T87. Small amounts of plastic deformation between solution treatment and aging had a significant effect on the thermograms. Aging experiments at 130 and 190 °C showed that the aging sequence and DSC response of this alloy were similar to those of pure Al-Cu when the increased copper content is taken into account. Further aging experiments at temperatures between room temperature and 130 °C showed pronounced changes of the GP zone dissolution peak as a function of aging conditions. These changes were found to be related to the effect of GP zone size on the metastable phase boundary and on the GP zone dissolution kinetics.