Temperature Dependence of Young's Modulus and Internal Friction in Alumina, Silicon Nitride, and Partially Stabilized Zirconia Ceramics |
| |
Authors: | Masahiko Shimada Ken'ichi Matsushita Shusei Kuratani Taira Okamoto Mjtsue Koizumi Koji Tsukuma Takaaki Tsukidate |
| |
Affiliation: | Institute of Scientific and Industrial Research, Osaka University, Ibaraki, Osaka 567, Japan;Department of Applied Chemistry, Faculty of Engineering, Tohoku University, Sendai, Miyagi 980, Japan;Research Laboratory, Toyo-soda Manufacturing Co. Ltd., Shinnanyo, Yamaguchi 746, Japan |
| |
Abstract: | The temperature dependence of Young's modulus and internal friction (Q−1)in alumina, silicon nitride, and partially stabilized zirconia (Y-PSZ) ceramics was studied. Little change in Q−1 was found for alumina, whereas Q−1 for silicon nitride ceramics increased above 700°C. The Q−1 of Y-PSZ increased markedly with increasing temperature up to a peak at ∼200°C. |
| |