Metal nanoparticle-embedded super porous poly(3-sulfopropyl methacrylate) cryogel for H2 production from chemical hydride hydrolysis

Poly(3-sulfopropyl methacrylate) (p(SPM)) cryogel was prepared under cryogenic conditions (T = −18 °C) and used as template for in situ metal nanoparticle preparation of Co, Ni and Cu. These metal nanoparticle-containing super macroporous cryogel composites were tested for H₂ production from hydrolysis of sodium borohydride (NaBH₄) and ammonia borane (AB). It was found that amongst p(SPM)-M (M: Co, Ni, and Cu) composite catalyst systems, the catalytic performances of Co- and Ni-containing p(SPM) cryogel composite catalyst systems were the same, however in hydrolysis of NH₃BH₃, the order of performance of the catalysts was Co > Ni > Cu. Interestingly, p(SPM)-Co cryogel composite demonstrated better catalytic performances in salt environments e.g., faster H₂ production rate in sea and tap water compared to DI water, and almost no effect of ionic strength of the solution medium was observed, but the salt types were found to affect the H₂ generation rate. Other parameters that affect H₂ production rate such as metal type, temperature, water source, salt concentration, amount of metal nanocatalyst and reusability were investigated. It was found that the hydrogen generation rate (HGR) was increased to 2836 ± 90 from 1000 ± 53 (ml H₂)(g of Co min)⁻¹ by multiple loading and reduction cycles of Co catalyst. Also, it was found that TOF values are highly temperature dependent, and increased to 15.1 ± 0.8 from 2.4 ± 0.1 (mol H₂)(mol catalyst min)⁻¹ by increasing the temperature from 30 to 70 °C. The activation energy, activation enthalpy and activation entropy were determined as 40.8 kJ (mol)⁻¹, 37.23 kJ (mol K)⁻¹, and −170.87 J (mol K)⁻¹, respectively, for the hydrolysis reaction of NaBH₄ with p(SPM)-Co catalyst system, and 25.03 kJ (mol)⁻¹, 22.41 kJ (mol K)⁻¹, and −182.8 J (mol K)⁻¹, respectively, for AB hydrolysis catalyzed by p(SPM)-Co composite system.