Plasma spray deposition of tri-layer environmental barrier coatings |
| |
| Affiliation: | 1. Key Laboratory of Inorganic Coating Materials CAS, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China;2. Research Center of Composite Materials, Shanghai University, Shanghai 200072, China;3. The State Key Lab of High Performance Ceramics and Superfine Microstructure, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Shanghai 200050, China |
| |
| Abstract: | An air plasma spray process has been used to deposit tri-layer environmental barrier coatings consisting of a silicon bond coat, a mullite inter-diffusion barrier, and a Yb2SiO5 top coat on SiC substrates. Solidified droplets in as-deposited Yb2SiO5 and mullite layers were discovered to be depleted in silicon. This led to the formation of an Yb2SiO5 + Yb2O3 two-phase top coat and 2:1 mullite (2Al2O3*SiO2) coat deposited from 3:2 mullite powder. The compositions were consistent with preferential silicon evaporation during transient plasma heating; a consequence of the high vapor pressure of silicon species at plasma temperatures. Annealing at 1300 °C resulted in internal bond coat oxidation of pore and splat surfaces, precipitation of Yb2O3 in the top coat, and transformation of 2:1 mullite to 3:2 mullite + Al2O3. Mud-cracks were found in the Yb2SiO5 layer and in precipitated Al2O3 due to the thermal expansion mismatch between these coating phases and the substrate. |
| |
| Keywords: | Environmental barrier coatings Ytterbium silicate |
| 本文献已被 ScienceDirect 等数据库收录！ |
|