A novel intumescent flame‐retardant epoxy resins system |
| |
| Authors: | Ming Gao Shousheng Yang |
| |
| Affiliation: | 1. Department of Environmental Engineering, North China University of Science and Technology, Yanjiao Beijing 101601, China;2. Department of Fire Control Engineering, Chinese People' Armed Police Forces Academy, Langfang 102800, People's Republic of China |
| |
| Abstract: | Pentaerythritol diphosphonate melamine–dicyandiamide–formaldehyde resin salt, a novel macromolecular intumescent flame retardants (IFR), was synthesized, and its structure was a caged bicyclic macromolecule containing phosphorus characterized by IR, NMR and element analysis. The flame retardancy and thermal behavior of a new IFR system for epoxy resin were investigated by LOI, UL‐94 test, TG, and IR. Activation energy for the decomposition of samples was obtained using Kissinger equation. 25% of weight of IFR were doped into epoxy resin to get 27.5 of LOI and UL 94 V‐0. The TG curves and IR spectra show that IFR decreases the initial decomposition temperature and the maximum weight loss rate of epoxy resin, and enhances the thermal stability of epoxy resin at high temperatures and char yield. The activation energy for epoxy resin containing IFR was decreased by 44.8 kJ/mol, which shows that IFR can catalyze decomposition of epoxy resin. © 2009 Wiley Periodicals, Inc. J Appl Polym Sci, 2010 |
| |
| Keywords: | epoxy resins degradation flame retardant synthesis TG |
|
|