VxMn(4 − x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH3

A series of vanadium based catalysts(VxMn(4-x)Mo3Ce3/Ti) with different vanadium(x wt.%) and manganese((4-x) wt.%) contents have been prepared by the wet impregnation method and investigated for selective catalytic reduction(SCR) of NO_x by NH_3 in the presence of 8 vol.% H_2O and 500 ppm V SO_2.The physicochemical characteristics of the catalysts were thoroughly characterized.The SCR of NO_x by NH_3(NH_3-SCR) activity, especially the low-temperature activity, significantly increased with increasing V_2O_5 content in the catalyst until the V_2O_5 content reached 1.5 wt.%, which corresponds well with the redox properties of the catalyst.All of the metal oxides were well dispersed and strongly interacted with each other on the catalyst surface.V mainly exists in the V~(5+)state in the catalysts.The strong synergistic effect between the vanadium and cerium species led to formation of more Ce~(3+)species, and that between the vanadium and manganese species contributed to formation of more manganese species with low valences.All of the catalysts exhibited strong acidity, while the redox properties determined the NH_3-SCR activity, especially the low-temperature activity.H_2O and SO_2 had severe inhibiting effects on the activity of V1.5Mn2.5Mo3Ce3/Ti.However, good H_2O and SO_2 resistance and high NO_x conversion by V1.5Mn2.5Mo3Ce3/Ti could be achieved in the presence of SO_2 and almost no decline was observed in a long-term test at 275℃ for 168 hr in the presence of SO_2 and H_2O, which can be attributed to the sulfate species formed on the catalyst surface.

VxMn(4-x)Mo3Ce3/Ti catalysts for selective catalytic reduction of NO by NH_3