| 高速钢W6Mo5Cr4V2的脱磷试验 |
| |
| 引用本文： | 刘守平 刘道弟. 高速钢W6Mo5Cr4V2的脱磷试验[J]. 特殊钢, 1998, 19(6): 27-30 |
| |
| 作者姓名： | 刘守平 刘道弟 |
| |
| 作者单位： | [1]重庆大学 [2]重庆特殊钢有限责任公司 |
| |
| 摘 要： | 在３０ｋｇ感应炉上用ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ（ＭｏＯ３）渣、ＭｏＣｌ６粉剂和Ａｌ－Ｃａ合金作脱磷剂对高速钢Ｗ６Ｍｏ５Ｃｒ４Ｖ２进行脱磷试验。结果表明，ＣａＯ－Ｎａ２ＣＯ３－ＣａＦ２－ＦｅｘＯ渣的脱磷效果最好，一般脱磷率可达２６％￣５６％。
|
| 关 键 词： | 高速钢 脱磷 炼钢 |
Study on Dephosphorization for High Speed Steel W6Mo5Cr4V2 |
| |
| Liu Shouping, Sun Shanchang and Yang Dexin. Study on Dephosphorization for High Speed Steel W6Mo5Cr4V2[J]. Special Steel, 1998, 19(6): 27-30 |
| |
| Authors: | Liu Shouping Sun Shanchang Yang Dexin |
| |
| Abstract: | The dephosphorization for high speed steel W6Mo5Cr4V2 using the dephosphorizing agents: CaO-Na2 CO3CaF2-FexO(MoO3 ) flux, powdered MoCl6 and Al-Ca alloy was tested in a 30kg induction furnace. The results showed that of all the agents teSted the CaO-Na2 Co3 -CaF2 -FexO flux was best for dephoophorization, in general the dephosphorizing rate was 26% ~ 56%. |
| |
| Keywords: | High Speed Steel W6Mo5Cr4V2 Dephosphorization |