Influence of Sr2+ on Calcium‐Deficient Hydroxyapatite Formation Kinetics and Morphology in Partially Amorphized α‐TCP

Hydration of partially amorphized α‐TCP powders with Sr²⁺ concentrations ranging from 0 to 10 mol% substitution for Ca²⁺ was analyzed by isothermal calorimetry and quantitative in‐situ XRD. Hydration of both crystalline α‐TCP and amorphous TCP (ATCP) forming CDHA was retarded to an increasing extent with increasing Sr²⁺ content. Sr²⁺ slightly reduced the crystallite size (XRD coherent scattering domains) of the CDHA formed during hydration, while the size of crystals visible under SEM was not noticeably affected. Reaction enthalpies of ΔH_{R(Sr‐α‐TCP→Sr‐CDHA)} = 122 ± 8 J/g_TCP and ΔH_{R(Sr‐ATCP→Sr‐CDHA)} = 257 ± 8 J/g_TCP were determined for the hydration of crystalline α‐TCP and ATCP containing 5 mol% Sr²⁺ substitution for Ca²⁺. This is comparable with the corresponding reaction enthalpies previously obtained for undoped samples, which are 106 ± 7 J/g_TCP for α‐TCP and 250 ± 7 J/g_TCP for ATCP.