RHEED studies of the growth of Si(001) by gas source MBE from disilane |
| |
Authors: | S M Mokler W K Liu N Ohtani and B A Joyce |
| |
Affiliation: | IRC Semiconductor Materials, The Blackett Laboratory, Imperial College, London SW7 2BZ, UK |
| |
Abstract: | The growth of Si(001) from a gas source molecular beam epitaxy system (Si-GSMBE) using disilane (Si2H6) was investigated using reflection high-energy electron diffraction (RHEED). The surface reconstructions occurring between 100 and 775°C were studied as a function of both substrate temperature and surface coverage. We report the first observation of (2x2) and c(4x4) reconstructions during growth at substrate temperatures near 645°C using Si2H6. All growth was found to be initiated by the formation of three-dimensional (3D) islands which coalesced at substrate temperatures above 600°C. The surface reconstruction was found to change from a disordered to an ordered (2x1)+(1x2) structure at 775°C via intermediate (2x2) and c(4x4) phases. Thereafter, growth was found to proceed in a 2D layer-by-layer fashion, as evidenced by the observation of RHEED intensity oscillations. This technique has been used, for the first time, to calibrate growth rates during Si-GSMBE. The intensity oscillations were measured as a function of both substrate temperature and incident beam flux. Strong and damped oscillations were observed between 610 and 680°C, in the two-dimensional growth regime. At higher temperatures, growth by step propagation dominated while at lower temperatures, growth became increasingly three-dimensional and consequently oscillations were weak or absent. Similarly, there was a minimum flux limit ( <0.16 SCCM), below which no oscillations were recorded. |
| |
Keywords: | |
本文献已被 ScienceDirect 等数据库收录! |
|