Evolution of Ti (C, N)-based cermet microstructures |
| |
引用本文: | 李晨辉,熊惟皓,余立新. Evolution of Ti (C, N)-based cermet microstructures[J]. 中国有色金属学会会刊, 2002, 12(2): 214-217 |
| |
作者姓名: | 李晨辉 熊惟皓 余立新 |
| |
作者单位: | StateKeyLaboratoryofDieandMouldTechnology,CollegeofMaterialsScienceandEngineering,HuazhongUniversityofScienceandTechnology,Wuhan430074,China |
| |
基金项目: | Project (5 0 0 740 17)supportedbytheNationalNaturalScienceFoundationofChina,project (19990 48714 )supportedbytheNationalDoctorateProgramFundofEducationMinistryofChina,project (992P0 3 3 2 )supportedbyKeyScienceandTechnologyDevelopmentFoundationofHube |
| |
摘 要: | Two series of Ti(C, N)-based cermet materials originating from the same chemical composition but with dif-ferent grain size distribution and sintered to different stages of the sintering cycle have been studied using SEM, TEM,EDX, and XRD. Much of the surrounding structure is formed during solid state sintering. During the solid state sintering, at first, the Mo and W rich (Ti, Mo, W)C inner rim is formed by the interaction among TiC, WC, and Mo2C; then the Mo and W lean (Ti, Mo, W)(C, N)outer rim is formed. During the liquid phase sintering, the outer rim of coarse grains grows rapidly throw a solution-reprecipitation process; aLso coarse grains grow by particle coalescence. The interface between coarse grain outer rim and binder is flat (crystal surface).
|
关 键 词: | 金属陶瓷 显微结构 钛 机械性能 |
Evolution of Ti(C,N)-based cermet microstructures |
| |
Abstract: | Two series of Ti(C,N)-based cermet materials originating from the same chemical composition but with different grain size distribution and sintered to different stages of the sintering cycle have been studied using SEM,TEM,EDX,and XRD.Much of the surrounding structure is formed during solid state sintering.During the solid state sintering,at first,the Mo and W rich (Ti,Mo,W)C inner rim is formed by the interaction among TiC,WC,and Mo2C;then the Mo and W lean (Ti,Mo,W)(C,N)outer rim is formed.During the liquid phase sintering,the outer rim of coarse grains grows rapidly throw a solution-reprecipitation process;also coarse grains grow by particle coalescence.The interface between coarse grain outer rim and binder is flat (crystal surface). |
| |
Keywords: | Ti(C N) cermet microstructure |