Tribological Performance of UHMWPE/GNPs Nanocomposite Coatings for Solid Lubrication in Bearing Applications

Ultra-high molecular weight polyethylene (UHMWPE)/ graphene nanoplatelets (GNPs) nanocomposite coatings were developed to reduce friction and wear in the absence of liquid lubrication. UHMWPE nanocomposite powders with different loadings (0.25, 1, and 2 wt.%) of GNPs were prepared and electrostatic spraying technique was then used to deposit the nanocomposite powders on aluminum alloy to form a thin coating. Friction and wear tests were conducted on the coatings against a flat-end pin, made of hardened tool steel to determine the best loading of GNPs. That was further tested to investigate the effect of sliding speed and contact pressure on its tribological properties and to establish coating operating limits. Results showed that UHMWPE nanocomposite coating reinforced with 1 wt.% GNPs showed the best tribological performance. It reduced wear rate by about 51% as compared to the pristine UHMWPE coating. The coating sustained a maximum sliding speed of 1 m/s at a contact pressure of 4 MPa equivalent to a pressure and velocity (PV) value of 4 MPa.m/s.