Effect of N,N′‐diphenyl adipamide on the formation of the β‐crystalline form in isotactic polypropylene

The polymorphic compositions and mechanical properties of isotactic polypropylene (iPP) samples nucleated by a selective β‐nucleating agent N,N′‐diphenyl adipamide (DPA)] were investigated with wide‐angle X‐ray diffraction, polarized light microscopy, scanning electron microscopy, and mechanical tests. It was found that β‐phase crystals emerged with the addition of DPA, and the relative proportion of the β‐crystalline form reached the maximum value of 0.97 with the addition of 0.1 wt % DPA. The curved lamellae in the β spherulites were like flowers. The β spherulites were etched more easily than α spherulites because amorphous regions were distributed inside the β spherulites. The Izod notched impact strength increased sharply with the addition of DPA and attained the maximum value of 7.30 kJ/m² (the value of blank iPP was 3.13 kJ/m²) with the addition of 0.1 wt % DPA. An analysis of the misfit factors between DPA and β‐iPP showed that β‐iPP could epitaxially crystallize on the DPA crystal well. © 2008 Wiley Periodicals, Inc. J Appl Polym Sci, 2009