Magnetic, Electrical and Thermodynamic Properties of UCuT
x
Al11?x
Alloys Where T = Mn, Fe and x=4 and 5 |
| |
Authors: | Wojciech Suski Adam Pikul Konrad Wochowski Andrzej Gilewski Tadeusz Mydlarz Dariusz Badurski |
| |
Affiliation: | 1. W. Trzebiatowski Institute of Low Temperature and Structure Research, Polish Academy of Sciences, P.O. Box 1410, 50-950, Wroc?aw 2, Poland 2. International Laboratory of High Magnetic Fields and Low Temperatures, P.O. Box 4714, 50-985, Wroc?aw 47, Poland
|
| |
Abstract: | The structure, magnetic, electrical, and thermodynamic properties of UCuT x Al11?x alloys, where T = Mn or Fe and x=4 or 5 are presented. The behavior of the Fe alloys is ferromagnetic-like with the Curie points amounting to 180 and 230 K, and the saturation magnetic moments under magnetic field of 5 T equal to 4.75 and 6.02 μB/f.u., respectively, whereas under a magnetic field of about 34 T the magnetic moments amount to 6.9 and 9.0 μB/f.u. for the alloys with x=4 and 5, respectively. The Curie points are reflected in the temperature dependence of the specific heat in which the anomalies are found at 180–200 and 230 K for alloys with x=4 and 5, respectively, however, it shows no reflection in the temperature dependence of the electrical resistivity. The field dependence of the magnetization at T=1.9 K for both compounds exhibits considerable hysteresis. There is a pronounced difference between ZFC and FC magnetization in its temperature dependence below the Curie point for materials with x=4 and 5. The Mn alloys exhibit ferrimagnetic-like character for which, supposedly, the interplay of the uranium and manganize sublattices is responsible. Magnetic transitions are determined at T N =300 (x=4) and 380 K (x=5). However, those anomalies do not find confirmation in the temperature dependence of the specific heat and the electrical resistivity. Magnetic moments determined at T=1.9 K and in a magnetic field of 5 T are very low and in both cases amount to about 0.35 μB/f.u. and these values are slightly higher in a magnetic field of 34 T reaching a value of about 1.5 μB/f.u. Also for the Mn alloys the clear difference between ZFC and FC magnetization in its temperature dependence below the Curie point is observed. |
| |
Keywords: | |
本文献已被 SpringerLink 等数据库收录! |
|