| 导辊裂纹的成因及消除 |
| |
| 引用本文： | 胡斌,毛劲松.导辊裂纹的成因及消除[J].金属材料与冶金工程,2002(3):28-30. |
| |
| 作者姓名： | 胡斌 毛劲松 |
| |
| 作者单位： | 涟源钢铁集团有限公司,湖南,娄底,417009 |
| |
| 摘 要： | 结合实际工况，找出导辊裂纹产生的主要原因及提出消除方法，理论分析与实践结果表明，加强水冷可解决导辊的热疲劳裂纹问题。
|
| 关 键 词： | 导辊 热疲劳 裂纹 轧制 磨损 |
| 文章编号： | 1005-6084(2002)03-0028-03 |
| 修稿时间： | 2002年3月10日 |
CAUSATION AND ELIMINATION OF ROLLER GUIDE'S CRACKS |
| |
| HU Bin,MAO Jinsong.CAUSATION AND ELIMINATION OF ROLLER GUIDE''S CRACKS[J].Metal Materials And Metallurgy Engineering,2002(3):28-30. |
| |
| Authors: | HU Bin MAO Jinsong |
| |
| Abstract: | According to working condition in practice, the main causation of guide roller's crack was found and then we knew how to clear it Hot fatigue crackswill be eliminated if they were under plenty of cool water and this conclusion has been proved via theory analysis and the result of test |
| |
| Keywords: | guide roller hot fatigue crack rolling |