Dispersion,Mechanical and Thermal Properties of Epoxy Resin Composites Filled with the Nanometer Carbon Black |
| |
Authors: | Ai-Jie Ma Weixing Chen Yonggang Hou Gai Zhang |
| |
Affiliation: | 1. School of Materials and Chemical Engineering, Xi'an Technological University , Xi'an , P.R. China aijie_ma@163.com;3. School of Materials and Chemical Engineering, Xi'an Technological University , Xi'an , P.R. China |
| |
Abstract: | The nanometer carbon black (CB) was employed to prepare epoxy resin/carbon black (EP/CB) composites by blending-casting method. The different modified methods of silicone coupling agent were used to improve the dispersion of CB in epoxy resin. The mechanical and thermal properties of EP/CB composites were investigated. Experimental results showed that the mechanical properties increased at first, but decreased with excessive addition of CB. When the mass fraction of CB was 2%, the mechanical properties were maximum. The use of modified CB significantly enhanced the mechanical properties of the composites. For given CB loading, the CB modified by pretreatment method displayed better dispersion in the epoxy resin than that of the direct mixing method. SEM observation revealed that the tensile fracture surface of the composite filled with 2 wt% modified CB held more microcracks than that of 5 wt% modified CB, and the formed microcracks could consume more energy of rupture, finally to have better tensile strength. DSC analysis showed that the glass transition temperature (Tg) of the composites increased with the increasing mass fraction of CB. |
| |
Keywords: | Carbon black Composites Epoxy resin Properties |
|
|