| Abstract: | Solid state rolling of semi-crystalline polymers is shown to be an effective method of producing high strength, high modulus tape at acceptable production rates. High density polyethylene tape was produced having a tensile strength exceeding 300 MPa and a tensile modulus of 8.7 GPa at production rates exceeding 8 m/min. A significant factor in producing highly oriented tape by the rolling process is roll temperature. Increasing the roll temperature from 25°C to 125°C not only increases the maximum extent of orientation achievable, but increases the mechanical properties at a given degree of thickness reduction. Internal frictional heat development limited the maximum thickness reduction ratio of polypropylene to 6.6:1. This reduction was reached by rolling at 150°C. The resultant tape had a tensile modulus of 5.1 GPa and a tensile strength of 300 MPa. |