Microwave dielectric properties of SnO2-doped CaSiO3 ceramics

SnO₂-doped CaSiO₃ ceramics were successfully synthesized by a solid-state method. Effects of different SnO₂ additions on the sintering behavior, microstructure and dielectric properties of Ca(Sn_1−xSi_x)O₃ (x=0.5–1.0) ceramics have been investigated. SnO₂ improved the densification process and expanded the sintering temperature range effectively. Moreover, Sn⁴⁺ substituting for Si⁴⁺ sites leads to the emergence of Ca₃SnSi₂O₉ phase, which has a positive effect on the dielectric properties of CaO–SiO₂–SnO₂ materials, especially the Qf value. The Ca(Sn_0.1Si_0.9)O₃ ceramics sintered at 1375 °C possessed good microwave dielectric properties: ε_r =7.92, Qf =58,000 GHz and τ_f=−42 ppm/°C. The Ca(Sn_0.4Si_0.6)O₃ ceramics sintered at 1450 °C also exhibited good microwave dielectric properties of ε_r=9.27, Qf=63,000 GHz, and τ_f=−52 ppm/°C. Thus, they are promising candidate materials for millimeter-wave devices.