Anodic stability of electrodeposited ruthenium: galvanostatic,thermogravimetric and X-ray photoelectron spectroscopy studies

The anodic stability of an electrodeposited ruthenium electrode was measured by anodic galvanostatic polarization in 0.5 mol dm^–3 H₂SO₄ solution. The role of water and adsorbed hydroxyl groups in electrode stability was determined by means of thermogravimetric analysis. A continuous weight loss due to water removal and condensation of hydroxyl groups was detected between 120 and 430 °C. The loss of a hydrous component of the oxide layer was in direct correlation with the increase of the anodic stability. Between 430 and 480 °C a weight gain was detected on the thermogravimetric curve. It was attributed to the formation of the ruthenium oxide layer in a higher oxidative state. This finding was confirmed by X-ray photoelectron spectroscopy measurements.