| Effect of P/M value on the preforms and microstructures of spray formed 70Si30Al alloy |
| |
| 作者姓名： | Yanguang Wei Baiqing Xiong Yongan Zhang Hongwei Liu Feng Wang Baohong Zhu |
| |
| 作者单位： | State Key Laboratory for Fabrication ＆ Processing of Nonferrous Metals, Beijing General Research Institute for Nonferrous Metals, Beijing 100088, China |
| |
| 基金项目： | 国家重点基础研究发展计划(973计划) |
| |
| 摘 要： | A novel 70Si30Al alloy was prepared by the spray forming process for electronic packaging materials. The effect of the ratio of atomization pressure to metal melt mass flux rate （P/M） on the preforms and microstructures of the spray-deposited 70Si30Al alloy was studied. The results indicate that the PIM value has a considerable influence on the formation of the preforms and the optimal value is in the range of 0.209-0.231 MPa/（kg.min^-1）. The microstructure of the spray formed 70Si30AI alloy is fine and homogenous. The primary silicon phases distributing in the aluminum matrix evenly are fine and irregular. The aluminum matrix is divided into two groups： supersaturated α-Al phase or α-Al phase and Al-Si pseudoeutectic phase or Al-Si eutectic phase.
|
| 关 键 词： | 70Si30Al硅铝合金 喷雾成形 雾化压力 P/M值 粗加工成品 显微结构 |
| 收稿时间： | 2006-06-05 |
Effect of P/M value on the preforms and microstructures of spray formed 70Si30Al alloy |
| |
| Yanguang Wei Baiqing Xiong Yongan Zhang Hongwei Liu Feng Wang Baohong Zhu.Effect of P/M value on the preforms and microstructures of spray formed 70Si30Al alloy[J].Journal of University of Science and Technology Beijing,2007,14(2):141-145. |
| |
| Authors: | Yanguang Wei Baiqing Xiong Yongan Zhang Hongwei Liu Feng Wang Baohong Zhu |
| |
| Affiliation: | State Key Laboratory for Fabrication & Processing of Nonferrous Metals, Beijing General Research Institute for Nonferrous Metals, Beijing 100088, China |
| |
| Abstract: | A novel 70S130Al alloy was prepared by the spray forming process for electronic packaging materials. The effect of the ratio of atomization pressure to metal melt mass flux rate (PIM) on the preforms and microstructures of the spray-deposited 70Si30Al alloy was studied. The results indicate that the PIM value has a considerable influence on the formation of the preforms and the optimal value is in the range of 0.209-0.231 Mpa/(kg·min-1). The microstructure of the spray formed 70Si30Al alloy is fine and homogenous. The primary silicon phases distributing in the aluminum matrix evenly are fine and irregular. The aluminum matrix is divided into two groups: supersaturated α-Al phase or α-Al phase and Al-Si pseudoeutectic phase or Al-Si eutectic phase. |
| |
| Keywords: | 70Si30Al alloy spray forming atomization pressure mass flux rate microstructure |