| 封端异氰酸酯的制备及其解封研究 |
| |
| 引用本文： | 李建明,王小妹,陈为都. 封端异氰酸酯的制备及其解封研究[J]. 粘接, 2011, 0(7): 54-57 |
| |
| 作者姓名： | 李建明 王小妹 陈为都 |
| |
| 作者单位： | 中山大学化学与化学工程学院,广东广州,510275 |
| |
| 摘 要： | 用甲乙酮肟(MEKO)对端NCO预聚体进行封端,考查了不同的封端率对端NCO预聚体黏度的影响.用TGA、DSC、TG-IR等对封端聚氨酯解封过程进行研究.实验结果表明,当封端聚氨酯中残余NCO%低于0.1%时,贮存期可达1年以上.H'NMR分析表明,端异氰酸酯封闭成功.MEKO封端的聚氧酯在105℃解封,与聚醚胺混合后...
|
| 关 键 词： | 甲乙酮肟 封端异氰酸酯 解封温度 剥离强度 |
Synthesis of blocked isocyanate and study of unblocking reaction |
| |
| LI Jian-ming,WANG Xiao-mei,CHEN Wei-dou. Synthesis of blocked isocyanate and study of unblocking reaction[J]. Adhesion in China, 2011, 0(7): 54-57 |
| |
| Authors: | LI Jian-ming WANG Xiao-mei CHEN Wei-dou |
| |
| Affiliation: | (School of Chemistry and Chemical Engineering,Sun Yat-Sen University,Guangzhou,Guangdong 510275,China) |
| |
| Abstract: | The isocyanate terminated prepolymer was blocked with methyl ethyl ketoximel （MEKO）,the effect of different blocking percentage on the prepolymer viscosity was studied.The unblocking reaction was characterized by TGA, DSC and TG-IR.Experiment results showed that when the NCO% is less than 0.1% the blocked isocyanate has good stability for overed year.The H＇NMR analysis showed that the prepolymer was successfully blocked and the unblocking temperature was 105 ℃.The blocked isocyanate was used in PET/VMCPP laminating when mixing with polyether amine,the PET/VMCPP laminate was activate at 1 10 ℃ for 1 hour, and the peeling strength reached 2.0 N/15mm. |
| |
| Keywords: | MEKO blocked isocyanate unblocking temperature peeling strength |