Structure and Certain Properties of Hot-Pressed Boron Carbide-Based Ceramic with Calcium-Silicon Additive

The influence which the composition of powder mixtures, the treatment conditions which the mixtures are subjected to, and the conditions under which the hot-pressed composite materials B₄C – (5-10 mass%) calcium-silicon are fabricated exert on the structure, nature of failure, and mechanical properties of these materials is investigated. Optimum properties are possessed by material containing 10 mass% of addition. It is shown that the structure, morphology, and dispersivity, as well as the nature of the distribution of the components that are added to the composite material (secondary phase) vary as the temperature of hot pressing changes. Maximal mechanical characteristics of the composite material (σ_bend = 560 MPa, K _1c = 4.7 MPa·m^1/2, HV = 37 GPa) are attained at hot-pressing temperatures in the range 2000-2100°C.