Flow stress and dynamic strain-ageing of β-transformed Zircaloy-4

The 0.2% yield stress of β-transformed Zircaloy-4 was found to be independent of prior-β grain size but varied as the inverse of the transformed β plate width. A dislocation loop expansion model originally proposed by Langford and Cohen [7] for cold-drawn iron wires is used to explain the inverse plate width dependence. Both air-cooled and water-quenched samples exhibited dynamic strain-ageing effects in approximately the same temperature range of 573 to 673 K: (a) a local minimum in strain-rate sensitivity is associated with a peak or an inflection point in the temperature dependence of the 0.2% yield stress for water-quenched or air-cooled samples respectively, and (b) yield drops were observed in strain rate change tests.