Effect of twinning on flow stress during initial stage of hot compression of twin roll cast Mg-5.51Zn-0.49Zr alloy |
| |
| Authors: | Zhi-yi Liu Jing Xu Yan-hui Hou and S B Kang |
| |
| Affiliation: | [1]Key Laboratory of Nonferrous Metal Materials Science and Engineering, Ministry of Education, Central South University, Changsha 410083, China [2]School of Materials Science and Engineering, Central South University, Changsha 410083, China [3]Korea Institute of Materials Science, Changwon, Korea |
| |
| Abstract: | A Thermecmastor-Z hot deformation simulator, optical microscopy, XRD and TEM were employed to characterize the flow stress behavior and microstructure of twin roll cast ZK60 magnesium alloy during initial stage of hot compression at elevated temperature of 300 ℃ and 400 ℃ and a given strain rate of 10~(-2)s~(-1). The results suggest that flow stress drop during initial stage of hot compression at 300℃, generally led by dynamic recrystallization, is attributed to twinning, correspondingly to dynamic recrystallization as deformation temperature is raised to 400 ℃. |
| |
| Keywords: | magnesium alloy basal slip non-basal slip twinning hot deformation recrystallization |
| 本文献已被 CNKI 维普 万方数据 SpringerLink 等数据库收录！ |
|