Polynary silicon arsenic chalcogenide glasses with high softening temperatures

The introduction of Ag in SiAsTe glasses permits the incorporation of Se, otherwise volatile and/or degradable as a constituent in Si-containing chalcogenide glasses. SiAsAgTeSe glasses exhibit much higher softening ranges and glass transition temperatures than encountered in known chalgogenide systems. A glass Si₃₅As₁₅Ag₁₀Te₂₀Se₂₀ had the viscosity log ν = 13 at about 500°C, as compared to 370°C for the base glass Si₃₅As₂₅Te₄₀, the viscosity of log ν = 9.8 at about 560°C, as compared to 442°C for the base glass. Phase separation occurs in the system SiAsAgTeSe and becomes manifest in two glass transitions indicated by changes in the slopes of the expansion curves and breaks in the softening point-composition relations. The existence and behavior SiAsAgTeSe glasses suggests the possible development of higher T_g i.r. transparencies and higher T_g semiconductor glasses than described so far.