| 热采注汽管线的腐蚀与安全性分析 |
| |
| 引用本文： | 温建萍,冯庆伟,温涛,卢鑫. 热采注汽管线的腐蚀与安全性分析[J]. 腐蚀科学与防护技术, 2003, 15(5): 304-306 |
| |
| 作者姓名： | 温建萍 冯庆伟 温涛 卢鑫 |
| |
| 作者单位： | 1. 南京航空航天大学材料学院,南京,210016
2. 胜利石油股份有限公司,东营,257000 |
| |
| 摘 要： | 对两段注汽管材料进行了宏观检察、化学成分、壁厚与管径测量、光学金相组织、常温机械性能、断口扫描电镜、能谱元素等试验分析.结果表明，注汽管材料的局部腐蚀主要是氧化-氯化腐蚀.强度校核表明，两段注汽管目前的壁厚已不能满足内压P=172 MPa、温度T=354℃的使用条件.
|
| 关 键 词： | 注汽管 氧化-氯化腐蚀 断口分析 |
| 文章编号： | 1002-6495(2003)05-0304-03 |
| 修稿时间： | 2002-07-07 |
ANALYSIS OF CORROSION AND SAFETY FOR STEAM-INJECTING PIPES |
| |
| WEN Jian-ping ,FENG Qing-wei ,WEN Tao ,LU Xin College of Material Science and Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing ,China, Shengli Petroleum Co.Ltd.,Dongying ,China. ANALYSIS OF CORROSION AND SAFETY FOR STEAM-INJECTING PIPES[J]. Corrosion Science and Protection Technology, 2003, 15(5): 304-306 |
| |
| Authors: | WEN Jian-ping FENG Qing-wei WEN Tao LU Xin College of Material Science Engineering Nanjing University of Aeronautics Astronautics Nanjing China Shengli Petroleum Co.Ltd. Dongying China |
| |
| Affiliation: | WEN Jian-ping 1,FENG Qing-wei 2,WEN Tao 2,LU Xin 2 1 College of Material Science and Engineering,Nanjing University of Aeronautics and Astronautics,Nanjing 210016,China, 2 Shengli Petroleum Co.Ltd.,Dongying 257000,China |
| |
| Abstract: | In this paper,a failure analysis was performed for materials of two section steam-injecting pipes,by means of examinations such as:macro-morphology、wall thickness and diameter、chemical composition、optical micrography、mechanical properties、scanning electron microscope(SEM) and EDS.The results show that the pipes suffered from an oxidation-chlorination corrosion.Residual strength caluculation shows that the wall thickness of the corroded two section steam-injecting pipes is below the requirement for further use according to the following designing criterion:P=17.2 MPa and T=354℃. |
| |
| Keywords: | steam-injecting pipe oxidation-chlorination corrosion failure analysis |