Hydrothermal Formation of Hydroxyapatite Layers on the Surface of Type-A Zeolite

Type-A zeolite evenly covered with hydroxyapatite thin layers was prepared using hydrothermal treatment at 120°C for 8 h under autogenous pressure. The hydroxyapatite needlelike nanocrystals, 100–200 nm in diameter and 30 nm in thickness, were grown under the reaction between discharged Ca²⁺ ions from type-A zeolite and PO₄³⁻ ions in (NH₄)₃PO₄ solution. The preferential orientations of the c -axis of hydroxyapatite crystals perpendicular to a zeolite surface were observed using transmission electron microscopy. The crystal structure of type-A zeolite was not destroyed under the reaction, but the surface morphology was changed only with complete covering of scaly hydroxyapatite particles.