Microwave dielectric properties and its compatibility with silver electrode of Li2MgTi3O8 ceramics

The effects of BaCu(B₂O₅) (BCB) additions on the sintering temperature and microwave dielectric properties of Li₂MgTi₃O₈ ceramic have been investigated. The pure Li₂MgTi₃O₈ ceramic shows a relative high sintering temperature (∼1000 °C) and good microwave dielectric properties as Q × f of 40,000 GHz, ?_r of 27.2, τ_f of 2.6 ppm/°C. It was found that the addition of a small amount of BCB can effectively lower the sintering temperature of Li₂MgTi₃O₈ ceramics from 1025 to 900 °C and induce no obvious degradation of the microwave dielectric properties. Typically, the 0.5 wt% BCB added Li₂MgTi₃O₈ ceramic sintered at 900 °C for 2 h exhibited good microwave dielectric properties of Q × f = 36,200 GHz (f = 7.31 GHz), ?_r = 26 and τ_f = −2 ppm/°C. Compatibility with Ag electrode indicates this material can be applied to low temperature-cofired ceramics (LTCC) devices.