Effects of Calcium Substitution on the Structural and Microwave Dielectric Characteristics of [(Pb1−xCax)1/2La1/2](Mg1/2Nb1/2)O3 Ceramics

The effects of calcium substitution on the structural and microwave dielectric characteristics of (Pb_{1? x} Ca _x )_1/2La_1/2](Mg_1/2Nb_1/2)O₃ ceramics (with x = 0.01–0.5) were investigated. All the materials were observed to have an ordered A(B_1/2^'B_1/2^")O₃-type perovskite structure; however, the space group of the structure changed from Fm 3 m to Pa 3 as the calcium content increased to x = 0.1, and then from Pa 3 to R 3¯ at the x = 0.5 composition. During the structural evolution, the lattice parameter of the perovskite cell decreased linearly, and the dielectric constant ( k ) also decreased, from k = 80 to k = 38. However, the product of the quality factor and the resonant frequency ( Q × f ) increased from 50 000 GHz to 90 000 GHz as the calcium content increased. Also, the temperature coefficient of resonant frequency (τ_?) gradually changed from 120 ppm/°C to ?40 ppm/°C as the calcium content increased. At the x = 0.3 composition, a combination of properties— k ～ 50, Q × f ～ 86 000 GHz, and τ_?～ 0 ppm/°C—can be obtained.