Effects of melt‐extension and annealing on row‐nucleated lamellar crystalline structure of HDPE films

The row‐nucleated lamellar crystalline structure of high‐density polyethylene (HDPE) films was prepared by applying elongation stress to HDPE melt during T‐die cast film extrusion and subsequently annealing the extruded films. This unusual crystalline structure was analyzed in terms of lamellar crystalline orientation, long‐period lamellar spacing, crystallite size, and degree of crystallinity. The contribution of melt‐extension represented by draw‐down‐ratio (DDR) to the overall orientation was found to be most noticeable than other processing variables. Meanwhile, the long‐period lamellar spacing, the crystallite size, and the degree of crystallinity were influenced predominantly by the annealing temperature. Finally, the processing (melt extension and annealing temperature) – structure (lamellar crystalline structure) – property (hard elasticity) relationship of HDPE films was investigated. © 2006 Wiley Periodicals, Inc. J Appl Polym Sci 103: 3326–3333, 2007