Optimizing structure,toughness and wear performance of 15 % Cr cold work cast tool steel

A series of six Cr-, Cr + Mo-, Cr + Mo + V cold work cast tool steels were produced and investigated for microstructure, impact toughness and both experimental and industrial abrasive wear. Grain refinement of the steel matrix even in as-cast condition was obtained on using 2.3 % Mo + 0.9 % V and that ensured increasing impact toughness and abrasion resistance. An optimum impact toughness of about 85 J-cm^?2 was obtained in air quenched (970°C) and tempered (450°C) Mo + V containing steels in which area fraction of carbides reached 38 %. The abrasion resistance improved in case of steels tempered at 250°C and had fine grain structure.