Fabrication and modification of cellulose acetate based mixed matrix membrane: Gas separation and physical properties

[Cellulose acetate (CA)-blend-multi walled carbon nano tubes (MWCNTs)] mixed matrix membranes (MMMs), [CA/polyethylene glycol (PEG)/MWCNTs] and [CA/styrene butadiene rubber (SBR)/MWCNTs] blend MMMs were prepared by solution casting method for gas separation applications using Tetrahydrofuran (THF) as solvent. Both raw-MWCNTs (R-MWCNTs) and functionalized carboxylic-MWCNTs (C-MWCNTs) were used in membrane preparation. The MWCNTs loading ratio and pressure effects on the gas separation performance of prepared membranes were investigated for pure He, N₂, CH₄ and CO₂ gases. Results indicated that utilizing C-MWCNT instead of R-MWCNTs in membrane fabrication has better performance and (CO₂/CH₄) and (CO₂/N₂) selectivity reached to 21.81 and 13.74 from 13.41 and 9.33 at 0.65 wt% of MWCNTs loading respectively. The effects of PEG and SBR on the gas transport performance and mechanical properties were also investigated. The highest CO₂/CH₄ selectivity at 2 bar pressure was reached to 53.98 for [CA/PEG/C-MWCNT] and 43.91 for [CA/SBR/C-MWCNT] blend MMMs at 0.5 wt% and 2 wt% MWCNTs loading ratio respectively. Moreover, increase of feed pressure led to membrane gas permeability and gas pair selectivity improvement for almost all prepared membranes. The mechanical properties analysis exhibited tensile modules improvement with increasing MWCNTs loading ratio and utilizing polymer blending.