Interaction of O2 with Pd single crystals in the range 1-150 Torr: Oxygen dissolution and reaction |
| |
Authors: | Jinyi Han |
| |
Affiliation: | School of Chemical Engineering, Purdue University, Forney Hall of Chemical Engineering, Room 116, 480 Stadium Mall Drive, West Lafayette, IN 47907-2100, United States |
| |
Abstract: | The interaction of O2 with Pd(1 1 1), Pd(1 1 0) and Pd(1 0 0) was studied in the pressure range 1-150 Torr by the techniques of temperature programmed decomposition (TPD), Auger electron spectroscopy (AES) and low energy electron diffraction (LEED). The oxidation of Pd was rate-determined by oxygen diffusion into Pd metal followed by the diffusion into PdO once the bulk oxide layer was formed. The dissolution of oxygen atoms into Pd metal followed the Mott-Cabrera model with diffusion coefficient 10−16 cm2 s−1 at 600 K and activation energy of 60-85 kJ mol−1. The bulk oxide phase was formed when a critical oxygen concentration was reached in the near-surface region. The formation of PdO was characterized by a decrease in the oxygen uptake rate, the complete fading of the metallic Pd LEED pattern and an atomic ratio O/Pd of 0.15-0.7 as measured by AES. The diffusion of oxygen through the bulk oxide layer again conformed to the Mott-Cabrera parabolic diffusion law with diffusion coefficient 10−18 cm2 s−1 at 600 K and activation energy of 111-116 kJ mol−1. The values for the diffusion coefficient and apparent activation energy increased as the surface atom density of the single crystals increased. |
| |
Keywords: | Palladium Palladium oxide Oxidation Oxygen Single crystal surfaces Temperature programmed decomposition |
本文献已被 ScienceDirect 等数据库收录! |
|