Strength and Phase Stability of Yttria-Ceria-Doped Tetragonal Zirconia/Alumina Composites Sintered and Hot Isostatically Pressed in Argon–Oxygen Gas Atmosphere

Yttria-ceria-doped tetragonal zirconia (Y,Ce)-TZP)/alumina (Al₂O₃) composites were fabricated by hot isostatic pressing at 1400° to 1450°C and 196 MPa in an Ar–O₂ atmosphere using the fine powders prepared by hydrolysis of ZrOCl₂ solution. The composites consisting of 25 wt% Al₂O₃ and tetragonal zirconia with compositions 4 mol% YO_1.5–4 mol% CeO₂–ZrO₂ and 2.5 mol% YO_1.5–5.5 mol% CeO₂–ZrO₂ exhibited mean fracture strength as high as 2000 MPa and were resistant to phase transformation under saturated water vapor pressure at 180°C (1 MPa). Postsintering hot isostatic pressing of (4Y, 4Ce)-TZP/Al₂O₃ and (2.5Y, 5.5Ce)-TZP/Al₂O₃ composites was useful to enhance the phase stability under hydrothermal conditions and strength.