| SA299钢冷脆行为的研究 |
| |
| 引用本文： | 阎相桥,类维生,姚枚.SA299钢冷脆行为的研究[J].材料科学与工艺,1992(Z1). |
| |
| 作者姓名： | 阎相桥 类维生 姚枚 |
| |
| 作者单位： | 哈尔滨工业大学，哈尔滨工业大学，哈尔滨工业大学 |
| |
| 摘 要： | 某锅炉厂生产的锅炉汽包,在冬季制造过程中发生破裂,汽包材料为 SA299钢,对断口的初步分析发现为脆性解理断口,据此认为是冷脆破坏。本文依据冷脆特征温度 Tc 的概念对 SA299钢的冷脆行为进行了细致的分析。
|
| 关 键 词： | SA299钢 解理断裂 冷脆破坏 |
Low-Temperature Brittleness of SA299 Steel. |
| |
| Yan Xiangqiao Lei Weisheng Yao Mei.Low-Temperature Brittleness of SA299 Steel.[J].Materials Science and Technology,1992(Z1). |
| |
| Authors: | Yan Xiangqiao Lei Weisheng Yao Mei |
| |
| Affiliation: | Harbin Institute of Technology |
| |
| Abstract: | This paper investigated the low-temperature brittleness of SA299 steel based on the concept of characteristic transition temperature of brittleness T_c~*which has been recommended as a new parameter reflecting the sensitivi- ty to cleavage fracture. |
| |
| Keywords: | SA299 steel cleavage fracture low-temperature brittleness |