| Mg-MOF-74对CO2/H2O的吸附性能 |
| |
| 引用本文： | 杜涛,龙渊,汤琦,李生璐,刘丽影.Mg-MOF-74对CO2/H2O的吸附性能[J].高等学校化学学报,2017,38(2):225. |
| |
| 作者姓名： | 杜涛 龙渊 汤琦 李生璐 刘丽影 |
| |
| 作者单位： | 东北大学国家环境保护生态工业重点实验室, 沈阳 110819 |
| |
| 基金项目： | 国家自然科学基金(批准号: 51474067, 51406029)、 教育部基本科研业务费(批准号: N150204015)、 辽宁省教育厅重点实验室基础研究项目(批准号: LZ2015032)和国家重点研究发展计划项目(批准号: 2016YFB0601301, 2016YFB0601305)资助 |
| |
| 摘 要： | 以Mg(NO3)2·6H2O和2,5-二羟基对苯二甲酸为原料, 采用溶剂热法制备了金属有机骨架材料Mg-MOF-74. 利用X射线衍射(XRD)、 红外光谱(FTIR)和扫描电子显微镜(SEM)等测试手段对其结构、 形貌和性能进行了分析, 并利用自制穿透实验装置研究了产物吸附CO2/H2O的性能. 结果表明: 合成的样品纯度高, 结构完整, 形貌规则有序, 具有较高的CO2吸附量. 双组分CO2/H2O穿透实验结果证实, 在水蒸气存在情况下, 与沸石13X相比, Mg-MOF-74仍具有较高的CO2吸附能力, 可用于分离高湿烟道气中的CO2.
|
| 关 键 词： | Mg-MOF-74 穿透实验 CO2/H2O双组分吸附 |
| 收稿时间： | 2016-08-16 |
Adsorption Property of Mg-MOF-74 for CO2/H2O† |
| |
| DU Tao,LONG Yuan,TANG Qi,LI Shenglu,LIU Liying.Adsorption Property of Mg-MOF-74 for CO2/H2O†[J].Chemical Research In Chinese Universities,2017,38(2):225. |
| |
| Authors: | DU Tao LONG Yuan TANG Qi LI Shenglu LIU Liying |
| |
| Affiliation: | State Environmental Protection Key Laboratory of Eco-Industry, Northeastern University, Shenyang 110819, China |
| |
| Abstract: | Mg-MOF-74 was synthesized through a solvothermal method using Mg( NO3 ) 2 ·6H2 O and 2,5-di-hydroxyterephthalic acid as raw materials. The product was then characterized via X-ray diffraction(XRD), Fourier transform infrared ( FTIR ) spectroscopy, scanning electron microscopy ( SEM ) and breakthrough experiments. The results show that pure Mg-MOF-74 with complete structure, regular morphology and excellent CO2 adsorption properties was prepared. It is confirmed in breakthrough experiments that the as-synthesized Mg-MOF-74 maintains a high CO2 adsorption properties in the presence of H2 O. Therefore, the prepared Mg-MOF-74 is a suitable candidate for capturing CO2 from wet flue gas stream. |
| |
| Keywords: | Mg-MOF-74 Breakthrough experiment CO2/H2 O binary adsorption |