| Abstract: | A jet type erosion-corrosion tester was developed for the erosion-corrosion investigation of high-chromium cast irons. During tests the size and the shape of particles in the slurry can be maintained stable. The jet velocity and attack angle can be accurately controlled. The repeatability and ranking consistency of the test results are satisfactory. The test parameters can be adjusted in a wide range, so that the tester can simulate various practical working conditions. Electrochemical test data can be automatically collected and processed. Dynamic polarization curves can be obtained during erosion-corrosion test, which can be used to study the dynamic corrosion characteristics.Two high chromium cast irons were studied in hot concentrated alkaline slurry. The results show that the erosioncorrosion mass loss rate and dynamic corrosion rate of 295Cr26 iron is lower than that of 185Cr13 under the conditions similar to alumyte processing. The mechanism of erosion-corrosion of 295Cr26 and 185Cr13 was studied by using the tester. The interaction between erosion and corrosion was also quantitatively evaluated. |