Strong Surface‐Bound Sulfur in Carbon Nanotube Bridged Hierarchical Mo2C‐Based MXene Nanosheets for Lithium–Sulfur Batteries

In this work, hydroxyl‐functionalized Mo₂C‐based MXene nanosheets are synthesized by facilely removing the Sn layer of Mo₂SnC. The hydroxyl‐functionalized surface of Mo₂C suppresses the shuttle effect of lithium polysulfides (LiPSs) through strong interaction between Mo atoms on the MXenes surface and LiPSs. Carbon nanotubes (CNTs) are further introduced into Mo₂C phase to enlarge the specific surface area of the composite, improve its electronic conductivity, and alleviate the volume change during discharging/charging. The strong surface‐bound sulfur in the hierarchical Mo₂C‐CNTs host can lead to a superior electrochemical performance in lithium–sulfur batteries. A large reversible capacity of ≈925 mAh g ^{? 1} is observed after 250 cycles at a current density of 0.1 C (1 C = 1675 mAh g^?1) with good rate capability. Notably, the electrodes with high loading amounts of sulfur can also deliver good electrochemical performances, i.e., initial reversible capacities of ≈1314 mAh g^?1 (2.4 mAh cm^?2), ≈1068 mAh g^?1 (3.7 mAh cm^?2), and ≈959 mAh g^?1 (5.3 mAh cm^?2) at various areal loading amounts of sulfur (1.8, 3.5, and 5.6 mg cm^?2) are also observed, respectively.