Inhibition of the reduction of Cr(VI) at the magnetite–water interface by calcium carbonate coatings

The effect of calcium carbonate coatings on the reduction of aqueous chromate on the magnetite(1 1 1) surface has been investigated using a combination of synchrotron based X-ray photoemission spectroscopy (PES) and X-ray absorption near edge structure (XANES) spectroscopy, along with laboratory-based powder X-ray diffraction (XRD) and scanning electron microscopy (SEM). CaCO₃ coatings (dominantly calcite with minor quantities of aragonite and vaterite) of thicknesses ranging from 10 Å to 20 m were grown on magnetite(1 1 1) surfaces by exposure to supersaturated aqueous solutions followed by evaporation of the solution—a process that mimics pore-water evaporation in vadose zones leading to the formation of caliche and calcium carbonate coatings on mineral grains. Coating thicknesses were determined from attenuation of the Fe 2p photoemission signal by the carbonate coating. For coatings less than 15 Å thick, Cr 2p photoemission and Cr L_II, L_III-edge XANES spectra show that chromate is reduced by the underlying magnetite surface; however, as the minimum coating thickness increases beyond 15 Å, the magnetite surface becomes passivated and further chromate reduction ceases. Our findings suggest that carbonate coatings on natural magnetite grains can significantly reduce or eliminate their ability to reduce Cr(VI), which is a toxic and highly mobile environmental contaminant.