| 环境诱导氢致断裂的非比例过载效应 |
| |
| 引用本文： | 曹卫杰,杨晓雷.环境诱导氢致断裂的非比例过载效应[J].中国腐蚀与防护学报,1996,16(3):181-186. |
| |
| 作者姓名： | 曹卫杰 杨晓雷 |
| |
| 作者单位： | 上海工程技术大学能源与环境工程研究所 |
| |
| 基金项目： | 国家自然科学基金,上海市高教科技发展基金 |
| |
| 摘 要： | 研究连续充氢条件下短时非比例过载对４２ＣｒＭｏ钢／０．５ｍｏｌ／Ｌ Ｈ２ＳＯ４体系氢致断裂寿命的影响。结果表明；短时非比例过载对于ＨＩＦ的影响较之比例过载更为严重
|
| 关 键 词： | 过载效应 氢致断裂 高强度钢 |
THE EFFECT OF NON-PROPORTIONAL OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE |
| |
| CAO Weijie,YANG Xiaolei,GAO Hua.THE EFFECT OF NON-PROPORTIONAL OVERLOADING ON ENVIRONMENTAL HYDROGEN INDUCED FRACTURE[J].Journal of Chinese Society For Corrosion and Protection,1996,16(3):181-186. |
| |
| Authors: | CAO Weijie YANG Xiaolei GAO Hua |
| |
| Affiliation: | Shanghai University of Engineering Science |
| |
| Abstract: | he effect of short period non-proportional overloading on environmental hydrogen induced fracture life of 42CrMo steel in 0.5 mol/L H2SO4solution was studied under continuous hydrogen charging condition.A weight loading system was employed in the study. Experimental results showed that non-proportional overloading might cause more severe retardation than proportional one. The mechanisms responsible for retardation of subsequent crack growth were discussed. The influence of overloading was dependent on integral effect of the following faCtors: (1) crack branching,which decreassed significantly the crack growth driving force; (2) residual compressive stresses existing in the overloading plastic zone, which reduced effective stress intensity factors; (3) effect of dislocation shielding on retarding hydrogen transportation as well as accumulation; and (4) overloading damage, which might shorten HIF life. |
| |
| Keywords: | Overloading effect Hydrogen induced fracture High strength steel |