热氧化磁控溅射金属锌膜合成一维ZnO纳米棒

利用退火热氧化射频磁控溅射金属锌膜的方法在Si(111)衬底上制备了一维Zn O纳米棒,同时用多种测试手段对样品的晶体结构、表面形貌和光学性能进行了研究.XRD,SEM和TEM的测试结果表明,Zn O纳米棒为单晶相六方纤锌矿结构,呈头簪状向外发散生长,直径在30～60 nm左右,其长度可达几μm.PL 谱测试结果表明:在波长为280 nm光的激发下,在372 nm处有强的近带边紫外光发射和516 nm处的较微弱深能级绿光发射.说明合成的一维Zn O纳米棒的结晶质量和光学性能优良

Synthesis of One-Dimensional ZnO Nanorods by Oxidating Zinc Films Deposited with Magnetron Sputtering

One-dimensional ZnO nanorods are synthesized by ox idating thin metal zinc films deposited on Si(111) substrates with radio frequen cy magnetron sputtering.The crystal structure,surface morphology,and optical pro perties of nanorods are investigated.X-ray diffraction(XRD) pattern,scanning el ectron microscopy(SEM),and transmission electron microscopy(TEM) analyses show t hat the synthesized single-crystal ZnO nanorods develop like hairpins along dif ferent radials,with a hexagonal wurtzite structure.The diameters of nanorods ran ge between 30 and 60nm and lengths up to micrometers.Photoluminescence(PL) analy sis shows that,under 280nm light excitation,a strong and sharp near band-edge U V light emission band at 372nm and a relatively weak green deep-level light emi ssion band at 516nm are observed from the ZnO nanorods,which indicates excellent crystallization and optical quality of the fabricated ZnO nanorods.