Sintering mechanisms of Yttria with different additives

The sintering behaviour of conventional yttria powder was investigated, with emphasis on the effect of sintering additives such as B₂O₃, YF₃, Al₂O₃, ZrO₂, and TiO₂, etc. at sintering temperatures from 1000 °C to 1600 °C. Powder shrinkage behaviour was analysed using a dilatometer. The powder sintering mechanisms were identified at different temperatures using powder isothermal shrinkage curves. This analysis showed that the sintering additives B₂O₃ and YF₃ could improve yttria sintering by changing the diffusion/sintering mechanisms at certain temperatures, while sintering additives TiO₂, Al₂O₃ and ZrO₂ appeared to retard the powder densification at temperatures around 1000 °C and are more suitable when used at temperatures in excess of 1300 °C. The powder with La₂O₃ added had the slowest densification rate throughout the test temperatures in this experiment and was also found to be more suitable when used at temperatures higher than 1550 °C.