High-capacity superconducting current leads of Y1Ba2Cu3O7−x

We have fabricated and measured a high-capacity superconducting current lead composed of a Y₁Ba₂Cu₃O_7?x cylinder, 20 cm long and 0.9 cm² cross section. A steady-state, d.c., critical current of 225 A at a temperature of 77 K was measured in this sample, using a voltage criterion of 2×10^?7 V/cm (p = 8×10^?10 ohm-cm). This current was limited by the currentinduced, self magnetic field. To our knowledge this is the largest d.c. critical current so far reported in a Y₁Ba₂Cu₃O_7?x sample and demonstrates the possibility of using hightemperature superconducting HTS materials for current leads to low-temperature superconducting LTS magnets or in power distribution systems.