Effect of curing and heat treatment history on the dynamic mechanical response and the pore structure of hardened cement paste

Results for the dynamic mechanical response of hcp (hardened cement paste) specimens as a function of the curing-heat treatment history are reported. The temperature range investigated is from ?160°C to +100°C. In the temperature range from +25°C to +100°C, specimens cured at room temperature (R-cured) show a partially irreversible transition (reduction) in E. There are two low temperature transitions: the “adsorbate transition” between ?160°C and ?6-°C, and the “capillary transition” between ?50°C and 0°C. Both of these transitions are significantly affected by the curing-heat treatment history. Furthermore, both the E-modulus and the BET (water) surface area decrease as the severity of heat treatment increases.