Processing and properties of polycrystalline cubic boron nitride reinforced by SiC whiskers

Dense polycrystalline cBN (PcBN)–SiCw composites were fabricated by a two-step method: First, SiO₂ was coated on the surface of cubic boron nitride (cBN) particles by the sol-gel method. Then, silicon carbide whisker (SiC_w)- coated cBN powder was prepared by carbon thermal reaction between SiO₂ and carbon powders at 1500°C for 2 hour. Then, cBN–SiC_w complex powders were sintered by high-pressure and high-temperature sintering technology using Al, B, and C as sintering additives. The phase compositions and microstructures of cBN–SiC_w composites were investigated by X-ray diffraction and scanning electron microscopy, respectively. It was found that the SiC_w and Al₃BC₃ had been fabricated by in situ reaction, which cannot only promote densification but also improve mechanical properties. The relative density of PcBN composites increased from 96.3% to 99.4% with increasing SiC_w contents from 5 to 20 wt%. Meanwhile, the Vickers hardness, fracture toughness and flexural strength of as-obtained composites exhibited a similar trend as that of relative density. The composite contained 20 wt% of SiC_w exhibited the highest Vickers hardness and fracture toughness of 42.7 ± 1.9 GPa and 6.52 ± 0.21 MPa?m^1/2, respectively. At the same time, the flexural strength reached 406 ± 21 MPa.