Enhancement of mechanical properties of hydroxyapatite coating prepared by electrophoretic deposition method

The addition of bio-inert ceramics such as alumina and zirconia can significantly improve the mechanical properties of hydroxyapatite bioactive coatings and increase their biocompatibility. In the present study, the surface of a titanium substrate was coated by the electrophoretic deposition method (EPD). Moreover, the reaction bonding process has been used to precipitate the nanocomposite containing the hydroxyapatite (HA), alumina, yitteria-stabilized zirconia (YSZ). The coating process was performed by an electrical power supply and a suspension of hydroxyapatite, aluminum, and YSZ nanopowders. For preparing a suspension consisting of 50% isopropanol and 50% acetone, 0.6 g/L of iodine was used as a stabilizer. Green and sintered coatings were analyzed by FE-SEM and XRD. In addition, the mechanical properties such as bonding strength, hardness, and toughness were measured. The hardness, bonding strength, and toughness of the HA coating were 107 ± 10.3 HV, 10.8 ± 3.2MPa, and 0.72MPa√m, respectively, while those of the HA-Al₂O₃-YSZ nanocomposite coating were 213 ± 1.8 HV, 35 ± 1.6MPa, and 1.6MPa√m, respectively.