Anomalies of ultrasonic velocity in high-Tc ceramics YBa2Cu3Oy and BiSrCaCu2Oy

Ultrasonic longitudinal velocity and adsorption have been measured in ceramic superconductors YBa₂Cu₃O_y with various porosity and also in BiSrCaCu₂O_y. A velocity drop of about 400 ppm was found at T_c only in the measurements on cooling. The magnitude of the velocity drop is anomalously large compared with the value expected from the thermodynamics. A hysteresis of velocity with respect to temperature was observed in all the samples studied. It is suggested that some structural change at pore size level is responsible for this phenomenon.