CBE growth of high-quality AlGaAs/GaAs heterostructures for HEMT applications

AlGaAs/GaAs heterostructures were grown by chemical beam epitaxy using triethylgallium, triisobutylaluminium and pure arsine in flow control mode with hydrogen as carrier gas. For substrate temperatures of 580°C and V/III ratios of 10, high quality AlGaAs layers are obtained; heterostructures show abrupt and smooth interfaces. Modulation doping with silicon evaporated from a conventional effusion cell gives two-dimensional electron gases with carrier densities up to 1×10¹² cm^-2. Mobilities of 70000 cm²/V·s are obtained at 77 K for carrier densities of 4×10¹¹ cm^-2. The lateral homogeneity of the heterostructures in layer thickness, composition and doping level is excellent. Perfect morphology with defect densities of about 100 cm^-2 is observed. High electron mobility transistors (gate length 0.3 nm) fabricated from quantum well structures show a transconductance of about 380 mS/mm.