Effects of mechanical alloying parameters on the microstructures of nanocrystalline Cu-5 wt% Cr alloy |
| |
Authors: | Kunyu Shi Lihong Xue Youwei Yan Tao Shen |
| |
Affiliation: | 1. State Key Laboratory of Materials Processing and Die & Mould Technology, Huazhong University of Science and Technology, Wuhan, 430074, China
|
| |
Abstract: | Nanocrystalline Cu-5 wt%Cr alloy powders were fabricated by mechanical alloying (MA). The effects of MA processing parameters on the crystallite size, solid solubility, and microstructures of the Cu-5 wt%Cr alloys were investigated including type and size distribution of the grinding medium and ball-topowder weight ratio (BPR). The results show that the crystallites were refined effectively and solid solubility of Cr in Cu was extended when heavier ball and higher BPR were adopted. The maximum solubility is extended up to 5.6 at% (namely 4.6 wt%) Cr in Cu by use of a combination of large and small size WC-Co balls with BPR of 30:1. A Cu-5 wt%Cr supersaturated solid solution alloy bulk is obtained by spark plasma sintering the as-milled powders at 900 °C for 5 min. |
| |
Keywords: | |
本文献已被 CNKI SpringerLink 等数据库收录! |